| عرض: | 600-2500 ملم | درجة: | 42Crmo JIS SCM440 |
|---|---|---|---|
| طلب: | لوحة الغلاية، لوحة الحاويات، لوحة السفينة | تقنية: | تدحرجت ساخنة |
| يكتب: | صفيحة فولاذية | معيار: | ASTM ، GB ، AISI ، JIS ، DIN |
| طول: | 1000-12000 مم ، كالشرط الخاص بك | سماكة: | 2.0-200mm |
| شكل: | صفيحة فولاذية مسطحة | ||
| إبراز: | Hot Rolled SCM440 alloy steel plate,42CrMo alloy steel plate 2200mm,JIS SCM440 steel plate 18mm,42CrMo alloy steel plate 2200mm,JIS SCM440 steel plate 18mm |
||
AISI 4140 Steel Round Bar: diameter 5mm – 400mm
ASTM 4140 Steel Plate: thickness 5 –500mm x width 200– 2300mm
SAE 4140 Steel Block: 210mm x 500-810mm
| ASTM A29/A29M | C | Si | Mn | P | S | Cr | Mo |
| 4140/G41400 | 0.35～0.40 | 0.20～0.35 | 0.70～0.90 | 0.025 Max | 0.025 Max | 0.80～1.10 | 0.18～0.25 |
| DIN 17220, EN 10083 | C | Si | Mn | P | S | Cr | Mo |
| 1.7225/42CrMo4 | 0.38～0.45 | ≤0.40 | 0.60～0.90 | 0.035 Max | 0.035 Max | 0.90～1.20 | 0.15～0.30 |
| GB/T 1229 | C | Si | Mn | P | S | Cr | Mo |
| 42CrMo | 0.38～0.45 | 0.17～0.37 | 0.50～0.80 | 0.030 Max | 0.030 Max | 0.90～1.20 | 0.15～0.25 |
| JIS G4105 | C | Si | Mn | P | S | Cr | Mo |
| SCM440 | 0.38～0.43 | 0.15～0.35 | 0.60～0.85 | 0.030 Max | 0.030 Max | 0.90～1.20 | 0.15～0.30 |
| USA | German | Japan | China | ISO |
| ASTM 29/A29M | DIN 17350 | JIS G4404 | GB/T 1229 | ISO 683/18 |
| 4140 | 1.7225/42CrMo4 | SCM440 | 42CrMo | 42CrMo4 |
Hardness, Rockwell C: 22 HRC, Density: 7.85kg/m3
Tensile strength: 655 MPa .
Melting point: 1416°C
Thermal expansion: 12.2 µm/m°C (20-100 ºC)
Elastic modulus: 190-210 GPa (at 25 ºC ).
Forging of 4140 steel should be carried out between 2200 and 1650 º F (1200 and 900 º C). The lower the finishing temperature from forging, the finer will be the grain size. This alloy steel should ideally not be forged below 1650 º F (900 º C) and should be slow cooled after forging in Oil or water.
Slowly heat to 800～8500 ºC, keep enough time, ensure heat thoroughly. then cooling in furnace to 480 ºC, then cool in air. After annealing, the hardness 92 HBS Max.
4140 Steel is usually used at 18-22 HRc, If needs, AISI 4140 alloy steel can be hardened or Quenching by cold work. Quenching medium: oil
/ ℃ tempering temperature: 205 ~ 649°C.
After tempering hardness HRC: 18-25 HRc.
AISI 4140 alloy steel used for Structural products. As below:
Oil and gas sector, like collets, connection rods, conveyor pins, stem assemblies, gears, Bearings
Quality assured by Our ISO 9001:2008 quality management system. Our all AISI 4140 steel all had by SEP 1921-84 ultrasonic inspection (UT Test). Quality Grade: E/e, D/d, C/c.
FAQ:
Q1: Are you a trading company or manufacturer?
we also have our own factory for steel raw material sales and machining.Apart from our own mill, we can also provide material from other mills based on customer's different requirement.
Q2:What is the major steel grade your company offer?
S50C/S55C/S45C/1.2311/718/1.2738/1.2316/1.2083/1.2312/1.2714/H13/H11/D2/D3/O1/O2/4140/4340/5140/8620/52100/M2/M35/M42, etc, in round bar, flat bar and plate, and also semi-finished or precision ground flat bars.
Q3:What service does ShengHe Metal Provide?
Apart from sales of raw materail, we do machining processing like cutting, milling, grinding, turning, peeling, drilling, CNC machining.
Q4: What do you do to control product quality?
Before loadnig into container, all product will go through pre-shipment inspection by our professional QC group. UT test shalled be applied to steel material, according to Sep 1921 C/c,D/d,or E/e level based on different type of steel.
Q5:What is your MOQ?
Our MOQ each order is around 25 Tons(one container), customer can mix different types of steel to reach this quantity.
Q6: Can we visit your company and factory?
Yes, warmly welcome! We can book the hotel for you before you come to China and arrange our driver to our airport to pick you up when you come.
اتصل شخص: Mr. Gao Ben
الهاتف :: +86-18068357371
الفاكس: 86-0510-88680060